FLEXIBLE POLYPROPYLENE |
| PROPERTY |
METHOD |
UNITS |
.3 |
.5 |
.75 |
1.0 |
1.5 |
|
Thickness |
ASTM D 5199 |
mm |
0.3 |
0.5 |
0.75 |
1.0 |
1.5 |
|
Polymer Type (1) |
ASTM D 1777 |
- |
FPP |
FPP |
FPP |
FPP |
FPP |
|
Specific Gravity |
ASTM D 792 |
g/cm3 |
.91 |
.91 |
.91 |
.91 |
.91 |
|
Tensile Strength at Yield (MD, TD) |
ASTM D 6693 IV |
kN/m |
5, 4 |
5, 4 |
5, 4 |
5, 4 |
5, 4 |
|
Tensile Strength at Break (MD, TD) |
ASTM D 6693 IV |
kN/m |
28, 22 |
28, 22 |
24, 20 |
22, 18 |
22, 22 |
|
Elongation at Break |
ASTM D 6693 IV |
% |
900 |
900 |
900 |
900 |
900 |
|
Tear Resistance (MD, TD) |
ASTM D 1004 C |
N |
25, 25 |
35, 35 |
45, 45 |
65, 65 |
65, 65 |
|
Puncture Resistance |
ASTM D 4833 |
N |
90 |
150 |
210 |
250 |
250 |
|
Water Vapour Transmission (23 C, 50% RH) |
ASTM E 96 |
g/m2/24hrs |
- |
- |
- |
0.1 - 0.12 |
- |
|
Methane (CH4)Transmission (23 C, 50% RH) |
- |
cc/m2/24hrs |
- |
- |
- |
- |
65 |
|
Carbon Black Content |
OEE 8.2.4-02-01 |
% |
2-3 |
2-3 |
2-3 |
2-3 |
2-3 |
|
OIT |
ASTM D 3895 |
minutes |
> 100 |
> 100 |
> 100 |
> 100 |
> 100 |