PHYSICAL PROPERTIES - HIGH STRENGTH POLYPROPYLENE
|
GEOTEXTILES HIGH STRENGTH (product prefix: GHS)
|
|
Polypropylene
|
|
PROPERTY
|
TEST METHOD
|
UNITS
|
35/ 35
|
70/ 70
|
70/ 105
|
|
Mass
|
ASTM D 5261
|
kg
|
220
|
386
|
525
|
|
Wide Width Tensile
|
ASTM D 4595
|
kN/ m
|
35 x 35
|
70 x 70
|
70 x 105
|
|
Wide Width Elongation
|
%
|
10 x 8
|
9 x 9
|
14 x 9
|
|
Trapezoidal Tear
|
ASTM D 4533
|
N
|
556 x 556
|
1000 x 1000
|
1110 x 1335
|
|
Grab Tensile
|
ASTM D 4632
|
N
|
1401 x 1335
|
2700 x 2300
|
-
|
|
Grab Elongation
|
ASTM D 4632
|
%
|
15 x 15
|
-
|
-
|
|
Puncture Strength
|
ASTM D 4833
|
N
|
668
|
1200
|
1155
|
|
Mullen Burst
|
ASTM D 3786, AS 2001.2.4 B
|
kPa
|
4481
|
> 8274
|
> 8273
|
|
Apparent Opening Size
|
ASTM D 4751 (dry)
|
mm
|
.425
|
.425
|
.425
|
|
Water Flow Rate
|
ASTM D 4491
|
l/ m2/ min
|
1200
|
42
|
810
|
|
UV Resistance
|
ASTM D 4355
|
% retained
|
80 (500 hrs)
|
80 (500 hrs)
|
80 (500 hrs)
|
|
Values are MARV (minimum average roll values), calculated as typical minus two standard deviations.
|
PHYSICAL PROPERTIES - HIGH STRENGTH POLYESTER
|
Polyester
|
|
PROPERTY
|
TEST
|
UNITS
|
150/ 50
|
150/ 150
|
200/ 50
|
200/ 200
|
300/ 50
|
300/ 100
|
|
Tensile MD (min)
|
ISO 10319
|
kN/ m
|
160
|
160
|
220
|
220
|
330
|
330
|
|
Tensile CD (min)
|
kN/ m
|
55
|
160
|
55
|
220
|
55
|
110
|
|
Elongation at Break MD
|
%
|
11
|
12
|
12
|
11
|
12
|
13
|
|
Elongation at Break CD
|
%
|
11
|
12
|
12
|
11
|
11
|
11
|
|
CBR
|
ISO 12236
|
kN
|
11
|
16
|
11
|
> 10
|
> 12
|
> 18
|
|
Cone Drop
|
ISO 918
|
mm
|
7
|
4
|
7
|
17
|
15
|
13
|
|
Characteristic Opening Size
|
ISO 12956
|
mm
|
0.30
|
0.20
|
0.25
|
0.46
|
0.11
|
0.11
|
|
Permeability
|
ISO 11058
|
m/ sec
|
0.04
|
0.02
|
0.04
|
0.05
|
0.02
|
0.015
|
|
Weight
|
|
g/ m2
|
340
|
510
|
450
|
770
|
660
|
760
|
|
Polyester
|
|
PROPERTY
|
TEST
|
UNITS
|
400/ 50
|
500/ 50
|
500/ 100
|
600/ 50
|
800/ 100
|
1000/ 100
|
|
Tensile MD (min)
|
ISO 10319
|
kN/ m
|
440
|
550
|
550
|
660
|
880
|
1106
|
|
Tensile CD (min)
|
kN/ m
|
55
|
55
|
110
|
55
|
110
|
110
|
|
Elongation at Break MD
|
%
|
12
|
13
|
13
|
13
|
13
|
8
|
|
Elongation at Break CD
|
%
|
12
|
11
|
11
|
11
|
12
|
8
|
|
CBR
|
ISO 12236
|
kN
|
11
|
> 8
|
> 8
|
11
|
11
|
11
|
|
Cone Drop
|
ISO 918
|
mm
|
13
|
18
|
18
|
15
|
8
|
|
|
Characteristic Opening Size
|
ISO 12956
|
mm
|
0.45
|
0.16
|
0.14
|
0.15
|
0.15
|
|
|
Permeability
|
ISO 11058
|
m/ sec
|
0.02
|
0.015
|
0.015
|
0.04
|
0.05
|
|
|
Weight
|
|
g/ m2
|
950
|
1100
|
1200
|
1340
|
1900
|
|
|
Values of polyester fabrics above are Typical = Mean or Average Value of all test data. |
The data in all tables is intended as guides only and is not intended as a warranty or guarantee. Permathene Ltd. reserves the right to change the specification contained herein without notice.